POLITEX - AKV
- Polyethylene film
- SBS / styrene butadiene styrene / - modified bitumen
- Reinforced base layer / non-woven polyester fabric/
- Colored mineral slate / shale / or polyethylene film
Application: Waterproofing of flat roofs, pitched roofs, the second top coat for repair of old roofs, first underlay for new roofs, a second top coat for new roofs over thermal insulation.
Benefits:
L
ightweight and flexible, strong and reliable, versatile, with a good aesthetic appearance, a variety of colors and shapes, saving labor and time, require no maintenance, durable.
R
oll waterproofing materials have a wide range of applications. As one layer coating - repair of old roofs, building foundations, basement walls, canals, new roofs, gas tanks for LPG, power substation KTP and others. Complete multilayer systems - for all kinds and types of roofs and engineering facilities / underground tanks, bridges, tunnels, roads, etc. /
T
he choice of the optimal variant of the waterproofing depends on several factors / as technological requirements, mechanical loads, weather conditions, etc. /, And therefore need to be made by a specialist - individually for each case.
IMPORTANT : Waterproofing rolls to be transported and stored vertically. Concrete basis on which to make, be smooth and pre-primed, clean and dry. Do not apply at ambient temperatures below -10 ° C
|
Parameters |
Test Method |
Measure |
POLITEX - AKB |
|||||||||||
|
2,5 kg/m2 without protective surface of slate chips |
3 kg/m2 without protective surface of slate chips |
3,5 kg/m2 without protection mineral powder |
4 kg/m2 without protective surface of slate chips |
4.5 kg/m2 without protective surface of slate chips |
5 kg/m2 without protective surface of slate chips |
5.5 kg/m2 without protective surface of slate chips |
3,5 kg/m2 with protective surface of slate chips |
4 kg/m2 with protective surface of slate chips |
4,5 kg/m2 with protective surface of slate chips |
5 kg/m2 with protective surface of slate chips |
5,5 kg/m2 with protective surface of slate chips |
|||
|
Type the basis |
- |
- |
Non-woven polyester fabric |
|||||||||||
|
Type of bitumen |
- |
- |
Modified: SBS |
|||||||||||
|
Width |
BDS ЕN 1848-1 |
cм |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
|
Mass per unit of area |
BDS ЕN 1849-1 |
kg/m2 |
2,7 ± 0,1 |
3,1 ± 0,1 |
3,6 ± 0,1 |
4,17 ± 0,1 |
4,5 |
5 |
5,5 |
3,6 ± 0,1 |
4,1 ± 0,1 |
5,2 ± 0,1 |
5 |
5,5 |
|
Tensile strength at break – longitudinal – cross |
BDS ЕN 12311-1 |
N/5cm |
800 540 |
1000 540 |
790 550 |
800 530 |
860 590 |
960 640 |
950 650 |
900 575 |
900 570 |
910 580 |
950 640 |
950 650 |
|
Elongation – longitudinal – cross |
BDS ЕN 12311-1 |
% |
39 40 |
41 49 |
43 54 |
45 56 |
45 55 |
44 45 |
42 42 |
38 46 |
40 40 |
38 40 |
43 44 |
42 43 |
|
Waterproof under pressure 0,7MPa for 24h |
BDS ЕN 1928 Method В |
- |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
impervious to water |
|
Flexibility at low temperatures |
BDS EN 1109 |
°C |
0 °C / minus 5 °C without changes |
|||||||||||
|
Heat resistance |
BDS EN 1110 |
°C |
+ 100 °C without drip |
|||||||||||
|
Resistance of ripping off the joints – longitudinal – cross |
BDS EN 12316-1 |
N/5cm |
100 69 |
148 80 |
109 78 |
109 78 |
141 89 |
150 90 |
150 90 |
135 85 |
124 80 |
150 90 |
150 90 |
150 90 |
|
Shear strength of splice – longitudinal – cross |
BDS EN 12317-1 |
N/5cm |
(break outside joints) 798 520 |
(break outside joints) 1010 540 |
(break outside joints) 800 540 |
(break outside joints) 800 520 |
(break outside joints) 860 590 |
(break outside joints) 960 645 |
(break outside joints) 950 650 |
(break outside joints) 930 575 |
(break outside joints) 900 570 |
(break outside joints) 900 590 |
(break outside joints) 950 645 |
(break outside joints) 950 655 |
|
Dimensional stability |
BDS EN 1107-1 Method В |
% |
- |
- |
- |
0,8 ± 0,02 |
0,8 ± 0,02 |
0,8 ± 0,02 |
0,8 ± 0,02 |
- |
- |
- |
0,8 ± 0,02 |
0,8 ± 0,02 |
|
Resistance static load |
BDS EN 12730 |
- |
- |
- |
- |
in 250 N without leakage |
in 250 N without leakage |
in 250 N without leakage |
in 250 N without leakage |
- |
- |
- |
in 250 N without leakage |
in 250 N without leakage |
|
Resistance tear |
BDS EN 12310-1 |
N |
- |
- |
- |
200 ± 5 |
200 ± 5 |
200 ± 5 |
200 ± 5 |
- |
- |
- |
200 ± 5 |
200 ± 5 |
|
Adhesion of minutes. pospka (weight loss) |
BDS EN 12039 |
% by weight |
- |
- |
- |
- |
- |
- |
- |
4,3 ± 0,1 |
5 ± 0,1 |
4,6 ± 0,1 |
4,7 ± 0,1 |
4,7 ± 0,1 |